The ASTM A specification covers cold and hot finished stainless steel bars and hot-rolled or extruded shapes. More specifically, the ASTM sp. ASTM A This specification covers hot- and cold-finished bars of stainless steel, including rounds, squares, and hexagons, and hot-rolled or extruded shapes. 30 Jul ASTM A Standard Specification for Stainless Steel Bars and Shapes_物理_ 自然科学_专业资料。Standard Specification for Stainless Steel.
|Published (Last):||19 March 2012|
|PDF File Size:||1.47 Mb|
|ePub File Size:||4.51 Mb|
|Price:||Free* [*Free Regsitration Required]|
B Maximum unless otherwise indicated.
This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and if not revised, either reapproved or withdrawn. In the event of failure, the lot represented shall be rejected except that, at the option of the manufacturer, each asgm in the lot may be tested for acceptance. The grain size shall be reported on a Certified Test Report.
F Tensile strength 70 ksi [ MPa] min permitted for extruded shapes. Originally approved in Please copy and paste this embed script to where you want to embed Embed Script.
Historical Version s – view previous versions of standard. If you feel that your comments have not received a fair hearing you should make your views known to astmm ASTM Committee on Standards, at the address shown below. The presence of these phases can be demonstrated by tests, typically involving metallography, impact toughness, or corrosion resistance, although the testing requirements may be different for different alloy grades.
ASTM A479 Specifications
Current edition approved Nov. There are standards covering high nickel, chromium, austenitic aetm, and heat-resisting alloy materials. Four grades of the stainless steel are available which includes austenitic, austenitic-ferritic, ferritic, and martensitic grades.
D See Supplementary Requirement S1. Approved November 1, Referenced Documents purchase separately The documents listed below axtm referenced within the subject standard but are not provided as part of the standard. Continued Tensile Strength, min, ksi [MPa] Condition annealed annealed annealed annealed annealed annealed Martensitic Grades annealed 1 2 3 tempered tempered normalized and tempered annealed tempered annealed quenched and tempered 60 70 65 60 70 70 Yield Strength,A min, ksi [MPa] Elongation in 2 in.
Materials for High-Temperature Service S1. Size px x x x x Permission rights to photocopy the standard may also be secured from the ASTM website www.
E American Welding Society designation. Combining values from the two systems may result in non-conformance with the standard. F Nitrogen content is to be reported for this grade.
The austenitic stainless steels shall be subjected to heat treatment and shall undergo corrosion test. We need your help! 4a79 are a non-profit group that run this website to share documents.
ASTM A479 Grade 316L annealed
The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Testing for Intermetallic Compounds 9. Your comments will receive careful consideration at a meeting of the responsible technical committee, which you may attend.
Product analysis tolerance provisions do not apply. C The material shall be capable of meeting the required reduction of area where listed, but actual measurement and reporting of the reduction of area are not required unless specified in the purchase order. The certification shall be positively relatable to the lot of material represented. Thank you for interesting in our services. Your comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM International Headquarters.
NOTE 2—Many, if not all, duplex stainless steels and some austenitic stainless steels will form intermetallic phases or compounds such as sigma, chi, and laves phases when exposed to temperatures below the specified annealing temperature or cooled slowly from a higher temperature during casting, welding, or annealing.
ASTM A Grade L annealed Stainless Steel – Matmatch
These phases can typically be removed by correct annealing and cooling practices. ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned in this standard. Approved May 1, Mechanical Properties Requirements 7. These phases can asfm a negative 4a79 on mechanical properties and corrosion resistance. For that reason, a minimum grain size has been required of the H grades created for optimum elevated temperature propertiesand a mandatory grain size test and report has been added for the non—H grades so that the information is available for those desiring to reclassify a non—H grade to H grade.
C Except as required for specific alloy type, molybdenum, titanium, nickel, cobalt, tantalum, nitrogen, and copper need not be reported but shall not be present in other than residual amounts, the intent being to prohibit substitution of one alloy type for another due to absence of control of the above named elements in certain alloys.
The analysis shall meet the requirements of Table 1. Stabilized grades with columbium or titanium added cannot be handled this way, since they would become destabilized due to columbium or titanium carbide solution, without subsequent reheating.
ASTM does not give any warranty express or implied or make any representation that the contents of this abstract are accurate, complete or up to date. Work Item s – proposed revisions of this standard. All austenitic stainless steels shall be capable of passing intergranular corrosion tests in the as-shipped condition. It is informational only and not an official part of the standard; the full text atm the standard astmm must be referred asmt for its use and application. A number in parentheses indicates the year of last reapproval.
This standard has been approved for use by agencies of the Department of Defense. We need your help to maintenance this website. Tests shall be performed in accordance with Practice E of Practices A J Annealed bars shall be capable qstm meeting the tempered condition requirements when heat treated.
The test method sreporting requirements, and acceptance criteria shall be agreed upon by the manufacturer and purchaser in the purchase agreement. Mechanical properties such as tensile strength, yield strength, elongation, and hardness shall be determined for the specimens subjected to normalized, tempered, annealed, and xstm conditions.
S S S S This abstract is a brief summary of the referenced standard.